DIE CASTING ALLOYS

Die casting alloys are normally non-ferrous, and there is a large number available with a wide range of physical and mechanical properties covering almost every conceivable application a designer might require.

Aluminum and zinc alloys are the most widely used, and are followed by magnesium, zinc-aluminum (AZ) alloys, copper, tin and lead.

Zinc, lead and tin based alloys are classified as low melting point metals, all melting at less than 725 o F (385 o C). Zinc-aluminum (ZA) alloys have a slightly higher melting range of 800 o F to 900 o F (426 o C to 482 o C). Aluminum and magnesium alloys are considered to be moderate melting point alloys, being cast in the 1150 o F to 1300 o F (621 o C to 704 o C) range. Copper alloys are considered to be high melting pint, over 1650 o F (899 o C). Low melting point alloys are cast in hot chamber machines. Intermediate and high melting point alloys are cast in cold chamber machines. In recent years, specially designed hot chamber machines for die casting magnesium alloys have come into use.
- - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - -

ALUMINUM ALLOYS

Aluminum die casting alloys (Table 1) are lightweight, offer good corrosion resistance, ease of casting, good mechanical properties and dimensional stability.

Although a variety of aluminum alloys made from primary or recycled metal can be die cast, most designers select standard alloys listed below:

360 -- Selected for best corrosion resistance. Special alloys for special applications are available, but their use usually entails significant cost premiums.

380 -- An alloy which provides the best combination of utility and cost.

383 & 384 -- These alloys are a modification of 380. Both provide better die filling, but with a moderate sacrifice in mechanical properties, such as toughness.

390 -- Selected for special applications where high strength, fluidity and wear-resistance/bearing properties are required.

413 (A13) -- Used for maximum pressure tightness and fluidity.
- - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - -

ZINC ALLOYS

Zinc base alloys (Table 2) are the easiest to die cast. Ductility is high and impact strength is excellent, making these alloys suitable for a wide range of products. Zinc alloys can be cast with thin walls and excellent surface smoothness making preparation for plating and painting relatively easy.

It is essential that only high purity (99.99 + 0/0) zinc metal be used in the formulation of alloys. Low limits on lead, tin and cadmium ensure the long-term integrity of the alloy¡¯s strength and dimensional stability.
- - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - -

ZINC-ALUMINUM (ZA) ALLOYS

ZA alloys represent a new family of zinc based die casting materials which contain higher aluminum content than standard zinc alloys. These alloys provide high strength characteristics plus high hardness and good bearing properties (Table 2) . Thin wall castability characteristics and die life are similar to zinc alloys. ZA-8 is recommended for hot chamber die casting, which ZA-12 and ZA-27 must be cast by the cold chamber die casting process. All ZA alloys offer similar creep properties and are superior to standard zinc alloys.

ZAMAK 2: This is the strongest and hardest ZAMAK alloy. Generally die cast, it is occasionally employed for gravity casting. ZAMAK 2 is not the widely used.

ZAMAK 3: This is the most used general purpose zinc die casting alloy, providing an excellent combination of strength, ductility and impact strength. It also provides excellent plating and finishing characteristics. This alloy is the designer's first choice for die casting applications.

ZAMAK 5: ZAMAK 5 should be considered when moderately greater hardness, strength and creep resistance over ZAMAK 3 is required.

ZAMAK 7: this is a high purity for of ZAMAK 3 with similar mechanical properties. However, ZAMAK 7 has higher ductility (for forming bending operations) and the highest casting fluidity of the ZAMAK family.

ZA-8: Provides strength, hardness and creep properties.

ZA-12: Provides excellent bearing properties with strength and hardness characteristics between ZA-8 and ZA-27, plus good dimensional stability properties and somewhat better castability than ZA-27.

ZA-27: Offers the highest mechanical properties of the ZA family and is, therefore, recommended when maximum performance is required.